Ekwivalenti
| DIN 1.7102 | AFNOR 54SiCr6 | BS 685 A57 | UNI 54SiCr6 | AISI 9254 | SAE 9254 |
| JIS SUP12 | EN 54SiCr6 | EN 1.7102 | GOST 60S2ChA | UNS G92540 |
Kompożizzjoni kimika
| C | Si | Mn | P | S | Cr | - |
| 0.51 - 0.59 | 1.2 - 1.6 | 0.5 - 0.8 | max 0.025 | max 0.025 | 0.5 - 0.8 | Cu flimkien ma' 10Sn < 0.6 |
Proprjetajiet Mekkaniċi
| Proprjetajiet | Kundizzjonijiet | ||
| T (grad) | Trattament | ||
| Densità (×1000 kg/m3) | 7.7-8.03 | 25 | |
| Proporzjon ta' Poisson | 0.27-0.30 | 25 | |
| Modulu Elastiku (GPa) | 190-210 | 25 | |
| Qawwa tat-tensjoni (Mpa) | 1158 | 25 | żejt imkessaħ, qamħ fin, ittemprat f'425 grad |
| Qawwa tar-Rendiment (Mpa) | 1034 | ||
| Titwil ( fil - mija ) | 15 | ||
| Tnaqqis fl-Erja ( fil - mija ) | 53 | ||
| Ebusija (HB) | 335 | 25 | żejt imkessaħ, qamħ fin, ittemprat f'425 grad |
Trattament tas-sħana
Ittemprar artab:
Saħħan sa 640-680C, kessaħ bil-mod fil-forn. Dan se jipproduċi ebusija Brinell massima ta '310.
Normalizzanti:
Temperatura: 850-880C, arja.
Ebusija:
Jibbies minn temperatura ta' 840-870C segwita mit-tifi taż-żejt.
Ittemprar:
Temperatura tat-tempra: 430-500C, arja.
Test u spezzjoni
Saħħa tal-istrixxa tal-azzar: Saħħa tat-tensjoni; Titwil;Ebusija
Ittestjar tal-istrixxa tal-azzar: test tal-liwi ripetut
Metallografija tal-istrixxa tal-azzar: saff ta 'dekarburizzazzjoni
Spezzjoni tal-wiċċ tal-istrixxa tal-azzar: ħruxija tal-wiċċ